81.16.Rf Nanoscale pattern formation
Refine
Has Fulltext
- yes (2)
Is part of the Bibliography
- yes (2)
Year of publication
- 2008 (2)
Document Type
- Doctoral Thesis (2)
Language
- English (2)
Keywords
- Adsorptionskinetik (1)
- Biegekristalltechnik (1)
- Epitaxie (1)
- Epitaxy (1)
- Facettierung (1)
- Heteroepitaxie (1)
- Heteroorganische Monolage (1)
- Koadsorbat (1)
- Kristallwachstum (1)
- Kubisch flächenzentriertes Gitter (1)
Institute
The role of elastic interactions, particularly for the self-organized formation of periodically faceted interfaces, was investigated in this thesis for archetype organic-metal interfaces. The cantilever bending technique was applied to study the change of surface stress upon formation of the interface between 3,4,9,10-perylene-tetracarboxylic-dianhydride (PTCDA) and Ag(111). This system is known to form a chemisorptive bonding. Indeed, the sign and the coverage-dependence of the surface stress change are in agreement to models and previous measurements of chemisorptive systems in literature. While the adsorption of molecules into the large domains is associated with a negative, i.e. compressive stress change, the formation of domain boundaries in the molecular layer induces a stress change of opposite sign, increasing the surface stress. The magnitude of the surface stress change of (-0.30 +- 0.10} N/m reflects a relatively weak binding of a PTCDA molecule to each individual single silver atom. It is emphasized, however, that if normalized to the surface stress change per molecule, this value corresponds to a stress change of (-2.2 +- 0.2) eV per molecule which is in the order of the suspected binding energy of this system. Therefore, these experiments reveal elastic interactions to be of significant order of magnitude for this system class. Thereby, they add a new point of view to the understanding of these interfaces. Besides, since the results are in agreement with the well-known properties of this interface, they establish the cantilever bending technique in the field of organic-metal interfaces. The mere existence of a bending of the sample implies an interesting detail for the PTCDA/Ag(111) interface in particular. It is the first experimental evidence for a structural change in the topmost substrate layers upon adsorption of PTCDA on Ag(111). Since such a modification has significant implications for the interpretation of other experimental results, a further investigation with more quantitative structural methods appears necessary. The main focus of this work, however, was on the investigation of the formation of the long-range ordered, self-organized faceted PTCDA/Ag(10 8 7) interface. Reciprocal space maps of this interface were recorded both by spot profile analysis low energy electron diffraction (SPA-LEED) and low energy electron microscopy (LEEM) in selected area LEED mode. Complementary to the reciprocal data, also microscopic real-space LEEM data were used to characterize the morphology of this interface. Six different facet faces ((111), (532), (743), (954), (13 9 5), and (542)) were observed for the preparation path of molecular adsorption on the substrate kept at 550 K. Facet-sensitive dark-field LEEM localized these facets to grow in homogeneous areas of microscopic extensions. If the pristine mesoscopic orientation locally deviates from the average orientation, e.g. in pristine step density, locally different facet types are formed, distorting the otherwise regular mesoscopic pattern. Hence, the original mesoscopic orientation of the substrate strongly determines the degree of order of the faceted surface and the facet species formed. The temperature-dependence of the interface formation was studied in a range between 418 K and 612 K in order to learn more about the kinetics of the process. Additional steeper facets of 27° inclination with respect to the (111) surface were observed in the low temperature regime. Furthermore, using facet-sensitive dark-field LEEM, spatial and size distributions of specific facets were studied for the different temperatures. The nucleation density of the facets did not depend on temperature and can therefore be concluded not to be limited by diffusion. Moreover, the facet dimensions were statistically analyzed. The total island size of the facets follows an exponential distribution, indicating a random growth mode in absence of any mutual facet interactions. While the length distribution of the facets also follows an exponential distribution, the width distribution is peaked, reflecting the high degree of lateral order. This anisotropy is temperature-dependent and occurs starting above 478 K substrate temperature during growth. The peaked distribution indicates the presence of a long-range interaction which leads to the structural order of the self-organized grating. The origin of this long-range interaction was investigated combining three complementary in-situ methods, all providing new insights into the formation of faceted organic-metal interfaces: the cantilever bending technique, high-resolution low energy electron diffraction (SPA-LEED), and microscopy (LEEM). The cantilever bending technique was applied for the first time to a faceting system at all. Below the faceting transition temperature the surface stress change associated with the formation of the PTCDA/Ag(10 8 7) interface resembles in shape and magnitude the one observed for the reference interface PTCDA/Ag(111). But above the transition temperature the absolute surface stress change of (-0.67 +- 0.10) N/m observed for the faceted PTCDA/Ag(10 8 7) interface is considerably larger than for the previous cases. Moreover, the stress change happens in distinguishable stages with a clearly resolvable fine structure of regimes of positive and negative stress changes. These different regimes of surface stress change can be correlated to different stages of the structural phase transition observed by the structural in-situ methods. Thereby, morphological objects (i.e. the facets) are assigned to a specific stress character. Thus, domains of different stress character can be identified on the surface. These stress domains are the prerequisite to apply continuum descriptions of the self-ordering process based on elastic interactions. Hence, the results are the first experimental verification that these continuum descriptions are indeed also applicable to the whole system class of faceting organic-metal interfaces. In conclusion, the results provide strong evidence for elastic interactions being the physical origin of long-range order for this system. In addition, the clear correlation of structural phase transition and surface stress change regimes suggests surface stress to play also an important role for the kinetics of the system. Indeed, the system seems to try to limit the overall stress change during the interface formation by forming facets of positive and negative stress character. Hence, the selection of specific facets could depend on the corresponding stress character. Furthermore, the system seems willing to re-facet at high coverages in order to prevent imperfect domain boundaries which are associated with an increase of surface stress. Finally, template-assisted growth of lateral, heterorganic nanostructures has been explored. Therefore, self-assembled monolayers as a second archetype class of molecules were grown on partially covered PTCDA/Ag(10 8 7) interfaces. Indeed, using standard surface science techniques, the basic principle of this growth scheme was confirmed to be successful.
In this PhD thesis, we study the heteroepitaxial crystal growth by means of Monte Carlo simulations. Of particular interest in this work is the influence of the lattice mismatch of the adsorbates relative to the substrate on surface structures. In the framework of an off-lattice model, we consider one monolayer of adsorbate and investigate the emerging nanopatterns in equilibrium and their formation during growth. In chapter 1, a brief introduction is given, which describes the role of computer simulations in the field of the physics of condensed matter. Chapter 2 is devoted to some technical basics of experimental methods of molecular beam epitaxy and the theoretical description. Before a model for the simulation can be designed, it is necessary to make some considerations of the single processes which occur during epitaxial growth. For that purpose we look at an experimental setup and extract the main microscopic processes. Afterwards a brief overview of different theoretical concepts describing that physical procedures is given. In chapter 3, the model used in the simulations is presented. The aim is to investigate the growth of an fcc crystal in the [111] direction. In order to keep the simulation times within a feasible limit a simple pair potential, the Lennard-Jones potential, with continuous particle positions is used, which are necessary to describe effects resulting from the atomic mismatch in the crystal. Furthermore the detailed algorithm is introduced which is based on the idea to calculate the barrier of each diffusion event and to use the barriers in a rejection-free method. Chapter 4 is attended to the simulation of equilibrium. The influence of different parameters on the emerging structures in the first monolayer upon the surface, which is completely covered with two adsorbate materials, is studied. Especially the competition between binding energy and strain leads to very interesting pattern formations like islands or stripes. In chapter 5 the results of growth simulations are presented. At first, we introduce a model in order to realize off-lattice Kinetic Monte Carlo simulations. Since the costs in simulation time are enormous, some simplifications in the calculation of diffusion barriers are necessary and therefore the previous model is supplemented with some elements from the so-called ball and spring model. The next point is devoted to the calculation of energy barriers followed by the presentation of the growth simulations. Binary systems with only one sort of adsorbate are investigated as well as ternary systems with two different adsorbates. Finally, a comparison to the equilibrium simulations is drawn. Chapter 6 contains some concluding remarks and gives an outlook to possible further investigations.